| 斷裂伸長率 | 7% | 密度 | 1.5g/cm3 | 彎曲強度 | 147.059MPa |
| 彎曲模量 | 1960.78MPa | 成型收縮率 | 0.7% | 特性級別 | 增強級 |
在線訂購支持
在線訂購說明
保障消費者權益，真正做到正品交易，杜絕假冒偽劣產品
021-58958519 13061808058(蔣先生) 13424755533(趙先生)
聯系上海松翰
| 021-58958519 | |
| 13061808058(蔣先生) | |
| 13424755533(趙先生) | |
| |
|
|
產品簡述
備注
備注:特性：礦物增強30%
詳細數據
訂購指南
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | |
| 基本性能 | 燃燒率 | UL94 | HB | ||
| 吸水率 | ASTM D-570 | 1.0 | % | ||
| 成型收縮率 | UBEmethod | 0.8 | % | ||
| 成型收縮率 | UBEmethod | 0.7 | % | ||
| 吸水率 | ASTM D-570 | 6.4 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.50 | ||
| 機械性能 | 斷裂下的延伸率 | 23° | ASTM D-638 | 7 | % |
| 1%變形下的壓縮強度 | 23° | ASTM D-695 | 300 | kgf/cm2 | |
| 彎曲彈性率 | 23° | ASTM D-790 | 20000 | kgf/cm2 | |
| 彎曲彈性率 | 23° | ASTM D-790 | 61000 | kgf/cm2 | |
| 熔點 | DSC | 215-225 | °C | ||
| 彎曲強度 | 23° | ASTM D-790 | 1500 | kgf/cm2 | |
| 擠剪強度 | 23° | ASTM D-732 | 720 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 90 | ||
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 55 | ||
| 1%變形下的壓縮強度 | 23° | ASTM D-695 | 170 | kgf/cm2 | |
| 抗沖擊強度 | -30° | ASTM D-256 | 3.5 | kgf.cm/cm | |
| 屈服下的伸張強度 | 23° | ASTM D-638 | 510 | kgf/cm2 | |
| 屈服下的伸張強度 | 23° | ASTM D-638 | 880 | kgf/cm2 | |
| 彎曲強度 | 23° | ASTM D-790 | 650 | kgf/cm2 | |
| 屈服下的伸張強度 | 80° | ASTM D-638 | 400 | kgf/cm2 | |
| 屈服下的伸張強 | -30° | ASTM D-638 | 1240 | kgf/cm2 | |
| 抗沖擊強度 | 23° | ASTM D-256 | 4.0 | kgf.cm/cm | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 105 | ||
| 抗沖擊強度 | 23° | ASTM D-256 | 14 | kgf.cm/cm | |
| 彎曲強度 | -30° | ASTM D-790 | 1850 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | ||
| 抗沖擊強度 | -30° | ASTM D-256 | 5.0 | kgf.cm/cm | |
| 斷裂下的延伸率 | 23° | ASTM D-638 | 5 | % | |
| TABER磨耗率 | ASTM D-1044 | 20 | mg | ||
| 電氣性能 | 絕緣耐力 | ASTM D-149 | 21 | KV/mm | |
| 介電常數 | 60HZ | ASTM D-150 | 4.4 | ||
| 介電損耗 | 106HZ | ASTM D-150 | 0.01 | ||
| 體積電阻率 | ASTM D-257 | 1012 | |||
| 抗電弧強度 | ASTM D-495 | 120 | S | ||
| IEC電路 | UL746 | 600+ | V | ||
| 介電常數 | 106HZ | ASTM D-150 | 4.0 | ||
| 介電損耗 | 60HZ | ASTM D-150 | 0.01 | ||
| 介電常數 | 103HZ | ASTM D-150 | 4.3 | ||
| 介電損耗 | 103HZ | ASTM D-150 | 0.01 | ||
| 體積電阻率 | ASTM D-257 | 1015 | |||
| 熱性能 | 熱變形溫度 | 18.6kgf/cm2 | ASTM D-648 | 160 | °C |
| 線性熱膨脹系數 | ASTM D-696 | 5 | X的10-5cm/cm/°C | ||
| 熱變形溫度 | 4.6kgf/cm2 | ASTM D-648 | 200 | °C | |