| 斷裂伸長率 | 580% | 拉伸強度 | 16MPa | 密度 | 0.918g/cm3 |
| 熔體流動速率 | 1g/10min | 維卡軟化點 | 103℃ | 規格級別 | 吹塑 |
| 加工級別 | 吹塑級 |
在線訂購支持
在線訂購說明
保障消費者權益，真正做到正品交易，杜絕假冒偽劣產品
021-58958519 13061808058(蔣先生) 13424755533(趙先生)
聯系上海松翰
| 021-58958519 | |
| 13061808058(蔣先生) | |
| 13424755533(趙先生) | |
| |
|
|
產品簡述
詳細數據
訂購指南
| 性能項目 | 試驗條件[狀態] | 測試方法 | 測試數據 | 數據單位 | ||||
| 基本性能 | 比重 | ASTM D-792 | 0.918 | g/cm3 | ||||
| 熔體流動速率 | 190℃/2.16kg | ASTM D-1238 | 1 | g/10min | ||||
| 機械性能 | 電影穿刺能源 | 20.3um | Internal Method | 3.39 | J | |||
| 電影穿刺能源 | 50.8um | Internal Method | 5.08 | J | ||||
| 電影穿刺力 | 20.3um | Internal Method | 40 | N | ||||
| 電影穿刺力 | 50.8um | Internal Method | 71.2 | N | ||||
| 電影穿刺抵抗 | 20.3um | Internal Method | 20.9 | J/cm3 | ||||
| 電影穿刺抵抗 | 50.8um | Internal Method | 13 | J/cm3 | ||||
| 電影韌性 | 20.3um | ASTM D-882 |
|
J/cm3 | ||||
| 電影韌性 | 50.8um | ASTM D-882 |
|
J/cm3 | ||||
| 割線模量-2% Secant | 20.3um | ASTM D-882 |
|
MPa | ||||
| 割線模量-2% Secant | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸屈服強度 | 20.3um | ASTM D-882 |
|
MPa | ||||
| 拉伸屈服強度 | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸斷裂強度 | 20.3um | ASTM D-882 |
|
MPa | ||||
| 拉伸斷裂強度 | 50.8um | ASTM D-882 |
|
MPa | ||||
| 拉伸斷裂伸長率 | 20.3um | ASTM D-882 |
|
% | ||||
| 拉伸斷裂伸長率 | 50.8um | ASTM D-882 |
|
% | ||||
| 落錘沖擊 | 20.3um | ASTM D-1709A | 94 | g | ||||
| 落錘沖擊 | 20.3um | ASTM D-1709B | <100 | g | ||||
| 落錘沖擊 | 50.8um | ASTM D-1709A | 130 | g | ||||
| 落錘沖擊 | 50.8um | ASTM D-1709B | 270 | g | ||||
| 埃爾曼多夫撕裂強度 | 20.3um | ASTM D-1922 |
|
g | ||||
| 埃爾曼多夫撕裂強度 | 50.8um | ASTM D-1922 |
|
g | ||||
| 密封起始溫度 | 20.3um | Internal Method | 110 | ℃ | ||||
| 密封起始溫度 | 50.8um | Internal Method | 120 | ℃ | ||||
| 密封強度 | 150℃，0.0203mm | Internal Method | 1000 | g | ||||
| 密封強度 | 150℃，0.0508mm | Internal Method | 2100 | g | ||||
| 熱性能 | 維卡軟化點 | ASTM D-1525 | 103 | ℃ | ||||
| 熔化溫度 | Internal Method | 124 | ℃ | |||||
| 光學性能 | 光澤度 | 20°，20.3um | ASTM D-2457 | 62 | ||||
| 光澤度 | 20°，50.8um | ASTM D-2457 | 90 | |||||
| 光澤度 | 45°，20.3um | ASTM D-2457 | 50 | |||||
| 光澤度 | 45°，50.8um | ASTM D-2457 | 61 | |||||
| 霧度 | 20.3um | ASTM D-1003 | 12 | % | ||||
| 霧度 | 50.8um | ASTM D-1003 | 18 | % | ||||